김서림 방지를 위한 Quaternary Ammonium Salt를 포함하는 UV 경화형 Urethane Acrylate Oligomer의 합성 및 특성평가

Abstract

V-curable urethane acrylate oligomer containing ammonium salts(AO), suitable for anti-fog (AF) coatings was synthesized. The expected AO structure was confirmed by FT-IR and 1H-NMR. This AO was then formulated with reactive monomers and photoinitiator to form coating formulas. In order to compare the UV-curing behavior of AO with conventional oligomers, the photopolymerization of AO and SK cytech EBECRYL(series urethane acrylates EB 8210 and EB 9260) were determined by photo-differential scanning calorimetry(Photo-DSC). The anti-fog properties of UV-cured AF coating were investigated by contact angle test and anti-fog test. Coating properties such as pencil hardness, pendulum hardness, gloss, and adhesion of the UV-cured films containing AO were estimated. The results showed that the concentration of AO in the coating formulation had a great influence on the anti-fog properties of UV-cured AF coating. Especially, UV-cured AF coating containing AO 65 wt.% showed excellent anti-fog properties without sacrificing other desirable properties such as pencil hardness and adhesion.|김서림 방지 코팅에 적합한 암모늄염을 함유하는 UV-경화성 우레탄 아크릴 레이트 올리고머(AO)를 합성 하였다. 예상되는 AO 구조는 FT-IR 및 1H-NMR에 의해 확인되었다. 이 AO는 반응성 단량체 및 광개시제로 제형화되어 코팅 제형을 형성 하였다. AO의 자외선 경화 거동과 기존의 올리고머를 비교하기 위해 AO 및 SK cytech 사의 EBECRYL series 중 계열 우레탄 아크릴 레이트 EB 8210 및 EB 9260의 광 중합을 Photo-Differential Scanning Calorimetry(Photo-DSC)로 경화거동을 확인하였다. 접촉각 시험 및 방담 시험으로 자외선 경화 AF 코팅의 김서림 방지 특성을 조사 하였다. 또한. AO가 함유 된 자외선 경화 필름의 연필 경도, 진자 경도, 광택도 및 접착력과 같은 코팅 특성을 조사했습니다. 결과적으로는 코팅 제제에서의 AO의 농도가 자외선 경화 된 AF 코팅의 김서림 방지 특성에 큰 영향을 미친다는 것을 보여 주었다. 특히, AO를 65 wt%를 함유하는 자외선 경화 된 AF 코팅은 연필 경도 및 접착력은 김서림 방지 특성을 잃지 않으면서 우수한 내구성 및 표면경도, 김서림 방지 특성을 나타냈다.