시효처리에 따른 Ti-7Zr-xNb 합금의

Metadata Downloads
Author(s)
이종한
Issued Date
2007
Abstract
Cp Ti and Ti-based alloys have been widely used for biomedical applications due to their biocompatibility superiority, mechanical properties and corrosion resistance. However, when implanted into human body these metals are problematic because they do not show direct bonding with living bone. Therefore, the purpose of this study is to investigate the microstructure variation and corrosion characteristics of Ti-7Zr-xNb alloys. Two kinds of alloys containing Nb concentrations of 5 and 10 wt% were used to investigate the microstructure, corrosion resistance and others. The specimens were solution treatment in the β phase field of Ti alloy and followed by water quenching(WQ). The samples for optical metallography, scanning electron microscopy were prepared using standard techniques and etched with Kroll's reagent. X-ray diffraction(XRD) analysis for specimens were performed using a philips 3121 diffractomenter. Effect of alloy composition on the corrosion resistance was studied by anodic polarization test. From the results of anodic polarization behavior in Ti-7Zr-xNb alloys, it was found that the corrosion resistance was increased with increasing Nb content.
Department
일반대학원 치의학과
Awarded Date
2008-02
Table Of Contents
LIST OF TABLES ⅱ
LIST OF FIGURES ⅲ
ABSTRACT ⅳ

제 1 장 서 론 1

제 2 장 이론적 배경 3
제 1절 생체용 Ti 합금 3
제 2절 전기화학적 부식 8

제 3 장 실험방법 11
제 1절 실험재료 11
제 2절 합금 제조 11
제 3절 용체화처리(solution treatment) 및 시효처리(aging treatment) 12
제 4절 미세조직 관찰 12
제 5절 전기화학적 부식 13

제 4 장 실험 결과 및 고찰 14
제 1절 생체용 Ti 합금의 용체화 처리에 따른 조직의 특성 14
제 2절 생체용 Ti 합금의 부식특성 평가 22

제 5 장 결 론 24

- 참 고 문 헌 - 25
Degree
Master
Publisher
조선대학교 대학원
Citation
이종한. (2007). 시효처리에 따른 Ti-7Zr-xNb 합금의.
Type
Dissertation
URI
https://oak.chosun.ac.kr/handle/2020.oak/7112
http://chosun.dcollection.net/common/orgView/200000236144
Appears in Collections:
General Graduate School > 3. Theses(Master)
Authorize & License
  • AuthorizeOpen
  • Embargo2008-02-19
Files in This Item:

Items in Repository are protected by copyright, with all rights reserved, unless otherwise indicated.