LED 광중합기의 조사 mode가 복합레진의 미세경도 및 수축응력에 미치는 영향
- Issued Date
- The purpose of this study was to evaluate the polymerization contraction and the microhardness of compostie resin(Supremer^(??), Filtek Flow^(??),3M-ESPE, USA) according to irradiation modes of LED curing unit(Elipar Highlight 2^(??), 3M-ESPE, USA).
The strain guage method was used for determination of polymerization contraction. Sample were divided by 6 groups according to curing modes and filling method.
Group A: Supreme^(??), Filtek Flow^(??) lining, 10seconds curing, Group B: Supreme^(??), Filtek Flow^(??) lining, 15seconds curing, Group C: Supreme^(??), Filtek Flow^(??) lining, 15seconds soft start curing, Group D: Supreme^(??) only, 10seconds curing, Group E: Supreme^(??) only, 15seconds curing, Group F: Supreme^(??) only, 15seconds soft start curing
Preparations of acrylic molds were followed by filling and curing. Strain guage attached to each sample were connected to a strainmeter. Measurements were recorded at each second for the total of 10 minutes including the periods of light application. And microhardness of each group after 24hours from light irradiation were measured.
Obtained data were analyzed statistically using ANOVA and Tukey test.
The results of the present study is as follows:
1.In flowable resin liner group, soft start curing group was not found decrease of polymerization contraction. But, In Supreme only filling group, the lowest polymeriation contraction was found in soft start curing group.
2.10 seconds curing group showed statistically significant reduction of polymerization contraction compared with 15 seconds curing group(p<0.05).
3.The microhardness values of each group not revealed significant difference(p>0.05). But, lower surface microhardness was not reached 80% of upper surface microhardness.