Fabrication of CuSn Nanofibers Prepared via Electrospinning

Abstract

The Cu and CuSn/PVP nanofibers were fabricated by electrospinning method by controlling various parameters. The precursor solution was prepared with copper(II) acetate monohydrate ($Cu(CH_3COO)_2$ 수식 이미지) and tin chloride dihydrate ($SnCl_2{\cdot}2H_2O$ 수식 이미지), and polyvinylpyrrolidone (PVP) for adjusting viscosity. The fabricated nanofibers were calcined at 873 K in Ar atmospheric environment for 5 hours to remove the solvent and polymer. The morphology and diameter of nanofibers were measured by optical microscopy (OM) with Motic image plus 2.0 program. The components and chemical environment were investigated with X-ray photoelectron spectroscopy (XPS). From the XPS survey spectra, we confirmed that CuSn/PVP nanofibers were successfully fabricated. The XPS peaks of C 1s and N 1s were remarkably decreased after calcination of the nanofibers at 873 K. It implies that the PVP was completely decomposed after calcination at 873 K.