인코넬 82, 52 적용 이종금속용접부의 미세조직 및 기계적 특성에 관한 연구

Abstract

The dissimilar metal welding makes the complicated structure by the dilution of the base metal and filler metal. That kinds of welding structure requires an evaluation on the mechanical characteristics. Moreover, HAZ (Heat affected zone) shows a phenomenon to decrease the tension with unstable structure along with the high residual stress. The dissimilar metal welding part improves the quality of the welding part by enhancing the characteristics of deposited metal through the filler metal structuring and modified structure control. Therefore, many studies to improve by evaluating the modified structure and mechanical characteristics of the dissimilar metal welding parts had been executed. However, the study on the changes in mechanical characteristics and modified structure of the dissimilar metal welding part consists of the low Alloy steel basic material and Alloy 82, 52 filler metals had not executed systematically so far. This study the changes in structure and mechanical characteristics by the analysis on mechanical characteristics of the welding part and the post weld heat treatment through the tensile strength, flexural strength and hardness test after checking the stability of the welding part with the non-destructive test as producing the low Alloy metal welding sample. |이종금속용접은 모재와 용가재 희석(dilution)에 의한 복잡한 조직이 발생되며 이러한 용접부 조직은 기계적 특성 평가가 요구된다. 또한 HAZ는 높은 잔류응력과 더불어 조직이 불안정하여 인성이 저하되는 현상이 나타난다. 이종금속용접부는 용가재 조성 및 미세조직 제어를 통하여 용착금속 특성을 향상시켜 용접부 품질을 향상 시킬 수 있다. 따라서 이종금속용접부의 미세조직 및 기계적 특성을 평가하여 개선하기 위한 많은 연구가 수행되었다. 그러나 저 합금강 모재와 Alloy 82, 52 용가재로 구성된 이종금속용접부의 기계적 특성 및 미세조직 변화에 대한 연구는 지금까지 체계적으로 수행되지 않았다. 본 연구에서는 저 합금강 용접 시편을 제작하여 비파괴시험을 통한 용접부 건전성 확인 후 인장강도, 굽힘강도, 경도시험을 하여 용접부 기계적 특성 분석과 후열처리에 따른 조직 및 기계적 특성 변화에 관하여 연구를 하였다.