수소규소화 반응을 통한 마이크로파-박리된 그래핀 옥사이드와 실리콘 나노와이어 하이브리머의 합성과 특성 분석
- Author(s)
- 신동희
- Issued Date
- 2015
- Abstract
- Silicon nanowire(SiNW)-graphene Hybrimer was synthesized from the reduced GO and SiNW via hydrosilylation in the presence of platinum catalyst. Single-crystalline SiNWs were fabricated by using an electroless metal assisted chemical etching of bulk silicon wafers with silver nanoparticles deposited by a spin-casting. The etching of SiNWs was carried out in an aqueous solutions of hydrofluoric acid and hydrogen peroxide. Free-standing SiNWs were then obtained using ultrasono-method in THF. GO was prepared by Hummer’s method and reduced by a microwave to give a reduced grapheme which was used for the synthesis of SiNW-graphene Hybrimer. The morphology of SiNW-graphene Hybrimers were characterized by EDS, TEM, and FE-SEM. Covalent bond between graphene and SiNW was confirmed by using XPS, Raman, and FTIR spectroscopy. BET measurement showed that SiNW-graphene Hybrimer has a mesoporous.
- Alternative Title
- Synthesis and Characterization of Microwave-Exfoliated Graphene Oxide and Silicon Nanowire Hybrimer via Hydrosilylation
- Alternative Author(s)
- Shin, Dong Hee
- Affiliation
- 조선대학교 화학과
- Department
- 일반대학원 화학과
- Advisor
- 손홍래
- Table Of Contents
- TABLE OF CONTENTS
TABLE OF CONTENTS ⅰ
LIST OF SYMBOLS AND ABBREVIATIONS ⅱ
LIST OF TABLES ⅲ
LIST OF SCHEMES ⅳ
LIST OF FIGURES ⅴ
ABSTRACT ⅵ
1.Introduction...1
2.Experimental Section...6
2.1.Generals...6
2.2.Synthesis...6
2.2.1.Synthesis of Silicon Nanowire(SiNW)...6
2.2.2.Synthesis of Microwave-Exfoliated Graphene Oxide(MEGO)...8
2.2.3.Synthesis of Silicon Nanowire with Microwave-Exfoliated Graphene Oxide via Hydrosilylation...9
3.Results and Discussion...11
3.1.measurements...11
3.2.Characterization of Silicon Nanowire(SiNW)...11
3.3.Characterization of Microwave-Exfoliated Graphene Oxide(MEGO)...19
3.4.Characterization of SiNW-MEGO Hybrimer...22
4.Conclusion...29
5.Reference...30
- Degree
- Master
- Publisher
- 조선대학교
- Citation
- 신동희. (2015). 수소규소화 반응을 통한 마이크로파-박리된 그래핀 옥사이드와 실리콘 나노와이어 하이브리머의 합성과 특성 분석.
- Type
- Dissertation
- URI
- https://oak.chosun.ac.kr/handle/2020.oak/12407
http://chosun.dcollection.net/common/orgView/200000264725
-
Appears in Collections:
- General Graduate School > 3. Theses(Master)
- Authorize & License
-
- AuthorizeOpen
- Embargo2015-02-25
- Files in This Item:
-
Items in Repository are protected by copyright, with all rights reserved, unless otherwise indicated.