분무열분해법으로 성장된 CdO:F 박막의 구조와 광학적 전기적 특성

Metadata Downloads
Author(s)
서지웅
Issued Date
2006
Abstract
CdO:F films were deposited on the glass substrates by spray pyrolysis.
Transparent and conducting CdO films prepared at substrate temperatures ranging from 400℃ to 520℃ were identified as CdO with a preferred (111) orientation. For the sample prepared at a substrate temperature of 450℃, the crystal structure of the CdO:F film was identified as cubic with lattice constant a0=4.695Å. The (200) plane of the CdO:F crystal grew more predominantly than the other planes, and its intensity increased with increasing up to 6wt.%, after which it decreased. The optical transmission of the sample deposited at a F concentration of 4 wt.% was about 70 % in the wavelength range form 500 nm to 800 nm. Optical transmission CdO:F films increased with increasing F concentration. The optical energy band gap of the CdO:F films deposited at a F concentration of 3 wt.% was 2.66 eV. The optical energy band gaps of the CdO:F films increased with increasing F concentration. Electric resistivity and carrier concentration of the CdO:F films deposited with a F concentration of 5 wt.% were 4.63 × 10-5cm and 2.51× 1019cm.
Alternative Title
Structural, Optical and Electrical Properties of CdO:F Films Deposited by Spray Pyrolysis
Alternative Author(s)
Seo, Ji-Woong
Affiliation
조선대학교 교육대학원
Department
교육대학원 물리교육
Advisor
서동주
Awarded Date
2006. 2
Table Of Contents
표목차 = ⅲ
그림목차 = ⅳ
ABSTRACT = ⅴ
Ⅰ. 서론 = 1
Ⅱ. 이론 = 3
A. 결정구조 = 3
B. 반도체의 광흡수 = 6
C. Hall 효과 = 8
Ⅲ. 실험 = 10
A. CdO:F 박막의 성장 = 10
B. CdO:F 박막의 특성측정 = 11
1. 박막의 결정 구조 = 11
2. 박막의 표면형태 및 조성비 = 12
3. 광투과율과 광흡수 측정 = 12
4. 박막의 전기적 특성 = 12
Ⅳ. 실험결과 및 고찰 = 14
A. CdO:F 박막의 결정 구조 = 14
B. CdO:F 박막의 표면형태 = 20
C. CdO:F 박막의 화학적 조성 = 22
D. CdO:F 박막의 광투과율과 광흡수 특성 = 24
E. CdO:F 박막의 전기적 특성 = 31
Ⅴ. 결론 = 32
참고문헌 = 34
Degree
Master
Publisher
조선대학교 교육대학원
Citation
서지웅. (2006). 분무열분해법으로 성장된 CdO:F 박막의 구조와 광학적 전기적 특성
Type
Dissertation
URI
https://oak.chosun.ac.kr/handle/2020.oak/4459
http://chosun.dcollection.net/common/orgView/200000232932
Appears in Collections:
Education > Theses(Master)(교육대학원)
Authorize & License
  • AuthorizeOpen
Files in This Item:

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.